| 19.Investigation of wire feeding speed, welding speed and preheating temperature on hardness and microstructure of weld in RQT 701-British steel produced by FCAW. A. Honarbakhsh-Raouf and H.R. Ghazvinloo (2010) Indian J.Sci.Technol. Vol. 3, Issue 5, pp: 588-591. Domain site: http://www.indjst.org. |
 
|
- Abstract
FCAW (flux-cored arc welding) is an arc welding process widely used in different industries to join the metals and
alloys. The present study focuses on the effect of FCAW-G process parameters on the hardness and microstructure of
weld in RQT 701-British steel having 5 mm thickness. In this study, effects of wire feeding speed, welding speed and
preheating temperature were investigated. Different samples were produced by employing wire feeding speed of 4.5, 6
and 7.5 m/min, welding speed of 30, 45 and 60 cm/min and preheating temperature of 200, 300 and 400C. After
welding process, brinel hardness (HB) test was performed on weld metal and the micro-structural evolution of weld was
analyzed by optical observations of the weld cross sections. Results were clearly illustrated that change in process
variables has significant effect on hardness, grain size and phases transformations in weld metal.
- Keywords: FCAW, RQT 701-British steel, welding parameters, hardness, microstructure, heat input
|
| |
|
|
|